Talsox® 9001 Formosa Kunststof Hdpe
| Warmtegeleidbaarheid: | 0.45 W/m·K |
|---|---|
| Flexural Modulus: | 1,000 MPa |
| Recycleerbaarheid: | 100% |
Petroteen LR734001 LyondellBasell HDPE
| Dichtheid (23°C): | 00,953 g/cm3 |
|---|---|
| Melt mass-flow rate (MFR) (190°C/2,16 kg): | 0.38 g/10 min |
| Verwerkingsmethode: | Uitdrijvingsslag het Vormen |
Purell PE GF4750 LyondellBasell HDPE
| Dichtheid (23°C): | 0.950 g/cm3 |
|---|---|
| Melt mass-flow rate (MFR) (190°C/2,16 kg): | 0.4 g/10 min |
| Verwerkingsmethode: | Uitdrijvingsslag het Vormen |
VIDEO
Purell Acp 5231d Lyondellbasell HDPE
| Dichtheid (23°C): | 00,952 g/cm3 |
|---|---|
| Melt mass-flow rate (MFR) (190°C/2,16 kg): | 0.3 g/10 min |
| Verwerkingsmethode: | Injectieslag het Vormen |
Purell ACP 6541A LyondellBasell HDPE
| Dichtheid (23°C): | 00,954 g/cm3 |
|---|---|
| Melt mass-flow rate (MFR) (190°C/2,16 kg): | 1.5 g/10 min |
| Verwerkingsmethode: | Injectievorming |
Icorene N2805-1000 Nat Lyondellbasell Hdpe
| Dichtheid (23°C): | 00,954 g/cm3 |
|---|---|
| Melt mass-flow rate (MFR) (190°C/2,16 kg): | 20 g/10 min |
| Verwerkingsmethode: | Injectievorming |
Purell Gb7260 Lyondellbasell Hdpe
| Dichtheid (23°C): | 00,96 g/cm3 |
|---|---|
| Melt mass-flow rate (MFR) (190°C/2,16 kg): | 8 g/10 min |
| Verwerkingsmethode: | Injectievorming |
Novatec Hdpe Hy430 Japan Polychem Corporation
| Dichtheid: | 00,956 g/cm3 |
|---|---|
| Melt mass-flow rate (MFR) (190°C/2,16 kg): | 1.1 g/10 min |
| Strandhardheid (D): | 67 |
Talsox® 8001 Formosa Kunststof Hdpe
| Dichtheid: | 0.948 g/cm3 |
|---|---|
| Smelte massa-stroom (MFR) (190°C/2,16 kg) 0,05 g/10 min: | 00,05 g/10 min |
| Vervaardiging: | Taiwan Formosa Plastics |
Alathon H6030 LyondellBasell HDPE
| Dichtheid (23°C): | 0.965 g/cm3 |
|---|---|
| Melt mass-flow rate (MFR) (190°C/2,16 kg): | 30 g/10 min |
| Gecoupleerde Izod Impact (23°C): | 21 J/m |