Talsox® 8010 Formosa Kunststof Hdpe
| Dichtheid: | 00,956 g/cm3 |
|---|---|
| Smelte massa-stroom (MFR) (190°C/2,16 kg) 0,05 g/10 min: | 1 g/10 min |
| Vervaardiging: | Taiwan Formosa Plastics |
Talsox® 7200 Formosa Kunststof Hdpe
| Dichtheid: | 00,955 g/cm3 |
|---|---|
| Smelte massa-stroom (MFR) (190°C/2,16 kg) 0,05 g/10 min: | 22 g/10 min |
| Vervaardiging: | Taiwan Formosa Plastics |
Talsox® 8001 Formosa Kunststof Hdpe
| Dichtheid: | 0.948 g/cm3 |
|---|---|
| Smelte massa-stroom (MFR) (190°C/2,16 kg) 0,05 g/10 min: | 00,05 g/10 min |
| Vervaardiging: | Taiwan Formosa Plastics |
Purell Gb7260 Lyondellbasell Hdpe
| Dichtheid (23°C): | 00,96 g/cm3 |
|---|---|
| Melt mass-flow rate (MFR) (190°C/2,16 kg): | 8 g/10 min |
| Verwerkingsmethode: | Injectievorming |
Icorene N2805-1000 Nat Lyondellbasell Hdpe
| Dichtheid (23°C): | 00,954 g/cm3 |
|---|---|
| Melt mass-flow rate (MFR) (190°C/2,16 kg): | 20 g/10 min |
| Verwerkingsmethode: | Injectievorming |
Purell ACP 6541A LyondellBasell HDPE
| Dichtheid (23°C): | 00,954 g/cm3 |
|---|---|
| Melt mass-flow rate (MFR) (190°C/2,16 kg): | 1.5 g/10 min |
| Verwerkingsmethode: | Injectievorming |
Lupolen 5261z Lyondellbasell Hdpe
| Dichtheid (23°C): | 00,954 g/cm3 |
|---|---|
| Melt mass-flow rate (MFR) (190°C/2,16 kg): | 0.2 g/10 min |
| Verwerkingsmethode: | Uitdrijvingsslag het Vormen |
Talsox® 9001 Formosa Kunststof Hdpe
| Warmtegeleidbaarheid: | 0.45 W/m·K |
|---|---|
| Flexural Modulus: | 1,000 MPa |
| Recycleerbaarheid: | 100% |
Talsox® 9003 Formosa Kunststof Hdpe
| Dichtheid: | 00,952 g/cm3 |
|---|---|
| Smelte massa-stroom (MFR) (190°C/2,16 kg) 0,05 g/10 min: | 0.25 g/10 min |
| Vervaardiging: | Taiwan Formosa Plastics |
Talsox® 8050 Formosa Kunststof Hdpe
| Dichtheid: | 00,96 g/cm3 |
|---|---|
| Smelte massa-stroom (MFR) (190°C/2,16 kg) 0,05 g/10 min: | 60 g/10 min |
| Vervaardiging: | Taiwan Formosa Plastics |