Prime Polymer Evolue Sp2020 Lldpe Geblazen Film
| Melt mass-flow rate (MFR): | 2.3 g/10 min |
|---|---|
| Dichtheid: | 0.916 g/cm3 |
| Verwerkingsmethode: | Opgeblazen film |
Prime Polymer Evolue Sp1510 Lldpe, geblazen film
| Melt mass-flow rate (MFR): | 1.0 g/10 min |
|---|---|
| Dichtheid: | 0.915 g/cm3 |
| Hardheid van de durometer (kust D, spuitvormd): | 55 |
Prime Polymer Evolue PE SP4020 Geblazen film
| Melt mass-flow rate (MFR): | 10,8 g/10 min |
|---|---|
| Dichtheid: | 0.937 g/cm3 |
| Verwerkingsmethode: | Opgeblazen film |
Prime Polymer Evolue PE SP2520 Geblazen film
| Melt mass-flow rate (MFR): | 10,9 g/10 min |
|---|---|
| Dichtheid: | 0.925 g/cm3 |
| Verwerkingsmethode: | Opgeblazen film |
Prime Polymer Evolue PE SP2320 Geblazen film
| Melt Mass-Flow Rate (MFR): | 1.9 g/10 min |
|---|---|
| Dichtheid: | 00,92 g/cm3 |
| Verwerkingsmethode: | Opgeblazen film |
Prime Polymer Evolue Sp1520 Geblazen film
| Melt mass-flow rate (MFR): | 2 g/10 min |
|---|---|
| Dichtheid: | 0.919 g/cm3 |
| Hardheid van de durometer (kust D, spuitvormd): | 54 |
Prime Polymer Evolue Sp0510 Lldpe Geblazen Film
| Melt mass-flow rate (MFR): | 1.2 g/10 min |
|---|---|
| Dichtheid: | 00,903 g/cm3 |
| Hardheid van de durometer (kust D, spuitvormd): | 50 |
Het product is bedoeld in de bijlage bij Verordening (EG) nr. 1907/2006 van het Europees Parlement en de Raad.
| Dichtheid (23°C): | 0.918 g/cm3 |
|---|---|
| Melt mass-flow rate (MFR) (190°C/2,16 kg): | 2 g/10 min |
| Verwerkingsmethode: | Blown Film Cast Film Film Extrusie |
EvolueTM SP2540 Prime Polymer Metallocene
| Melt mass-flow rate (MFR): | 30,8 g/10 min |
|---|---|
| Dichtheid: | 0.924 g/cm3 |
| Verwerkingsmethode: | gegoten film |
EvolueTM Sp0540 Prime Polymer Mlldpe
| Melt mass-flow rate (MFR): | 30,8 g/10 min |
|---|---|
| Dichtheid: | 00,903 g/cm3 |
| Hardheid van de durometer (kust D, spuitvormd): | 49 |