Biobased suikerriet LLDPE lineaire polyethyleengranulaten met lage dichtheid Braskem LH0820/30AF
| Dichtheid (23°C): | 0.918 g/cm3 |
|---|---|
| Melt mass-flow rate (MFR) (190°C/2,16 kg): | 00,8 g/10 min |
| Verwerkingsmethode: | Geblazen film, filmextrusie |
Braskem Groen PE SLH118/21 LLDPE Materiaal Biobased Sugarcane Polyethyleengranules
| Dichtheid (23°C): | 0.918 g/cm3 |
|---|---|
| Melt mass-flow rate (MFR) (190°C/2,16 kg): | 1 g/10 min |
| Verwerkingsmethode: | Geblazen film extrusie. |
Biobased Polyethyleen Suikerriet LLDPE Granulaten Braskem Groen PE SLH118
| Dichtheid (23°C): | 0.916 g/cm3 |
|---|---|
| Melt mass-flow rate (MFR) (190°C/2,16 kg): | 1 g/10 min |
| Verwerkingsmethode: | Geblazen film extrusie. |
Braskem Green PE SLL118 Biobased Sugarcane Polyethyleen LLDPE Plastic Granules
| Dichtheid (23°C): | 0.916 g/cm3 |
|---|---|
| Melt mass-flow rate (MFR) (190°C/2,16 kg): | 1 g/10 min |
| Verwerkingsmethode: | Geblazen film extrusie. |
Polyethyleen LLDPE Granulaat Biobased Sugarcane Braskem Groen PE SLL318
| Dichtheid (23°C): | 0.918 g/cm3 |
|---|---|
| Melt mass-flow rate (MFR) (190°C/2,16 kg): | 2.7 g/10 min |
| Het vormen temperatuur: | 170 -180 °C |
HANWHA 3120 Hanwha Chemisch LLDPE
| Density: | 0.920 g/cm³ |
|---|---|
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg): | 1.0 g/10 min |
| Melt Temperature: | 150 to 190 °C |
Petrothene® Ga50224 LyondellBasell LLDPE
| Dichtheid (23°C): | 0.918 g/cm3 |
|---|---|
| Melt mass-flow rate (MFR) (190°C/2,16 kg): | 2 g/10 min |
| Verwerkingsmethode: | Blown Film Cast Film Film Extrusie |
Het product is bedoeld in de bijlage bij Verordening (EG) nr. 1907/2006 van het Europees Parlement en de Raad.
| Dichtheid (23°C): | 0.918 g/cm3 |
|---|---|
| Melt mass-flow rate (MFR) (190°C/2,16 kg): | 2 g/10 min |
| Verwerkingsmethode: | Blown Film Cast Film Film Extrusie |
Petroteen GA502022 LyondellBasell LLDPE
| Dichtheid (23°C): | 0.918 g/cm3 |
|---|---|
| Melt mass-flow rate (MFR) (190°C/2,16 kg): | 2 g/10 min |
| Verwerkingsmethode: | Blown Film Cast Film Film Extrusie |
Prime Polymer Evolue Sp1520 Geblazen film
| Melt mass-flow rate (MFR): | 2 g/10 min |
|---|---|
| Dichtheid: | 0.919 g/cm3 |
| Hardheid van de durometer (kust D, spuitvormd): | 54 |