Petrothene® NA143063 LyondellBasell LDPE
| Dichtheid: | 0.922 g/cm3 |
|---|---|
| Smelte doorstroming (MFR) (190°C/2,16 kg): | 2 g/10 min |
| Verwerkingsprocédés: | Extrusie, geblazen film |
Petrothene® Na209009 Lyondellbasell Ldpe
| Dichtheid: | 0.925 g/cm3 |
|---|---|
| Smelte doorstroming (MFR) (190°C/2,16 kg): | 23 g/10 min |
| Verwerkingsprocédés: | Extrusie, geblazen film |
Petrothene® NA206000 LyondellBasell LDPE
| Dichtheid: | 0.918 g/cm3 |
|---|---|
| Smelte doorstroming (MFR) (190°C/2,16 kg): | 14 g/10 min |
| Verwerkingsprocédés: | Extrusie, geblazen film |
Petrothene® NA205000 LyondellBasell LDPE
| Dichtheid: | 0.918 g/cm3 |
|---|---|
| Smelte doorstroming (MFR) (190°C/2,16 kg): | 16 g/10 min |
| Verwerkingsprocédés: | Extrusie, geblazen film |
Biologische suikerriet LDPE-polyethyleengranulaat Groen PE-knoop SBB0323
| Dichtheid (23°C): | 0.923 g/cm3 |
|---|---|
| Melt mass-flow rate (MFR) (190°C/2,16 kg): | 0.32 g/10 min |
| Het vormen temperatuur: | 170 -190 °C |
Petrothene® Na204000 Lyondellbasell LDPE
| Dichtheid: | 0.918 g/cm3 |
|---|---|
| Smelte doorstroming (MFR) (190°C/2,16 kg): | 7 g/10 min |
| Verwerkingsprocédés: | Extrusie, geblazen film |
Groen PE Braskem SBF0323/12HC Biobased Polyethyleengranules LDPE suikerrietmateriaal
| Dichtheid (23°C): | 0.923 g/cm3 |
|---|---|
| Melt mass-flow rate (MFR) (190°C/2,16 kg): | 0.32 g/10 min |
| Het vormen temperatuur: | 170 -190 °C |
Braskem Groen PE Seb853 LDPE Deeltjes Hoogdruk Biobased suikerrietmateriaal
| Dichtheid (23°C): | 0.923 g/cm3 |
|---|---|
| Melt mass-flow rate (MFR) (190°C/2,16 kg): | 2.7 g/10 min |
| Het vormen temperatuur: | 170 -190 °C |
Biobased polyethyleen LDPE deeltjes Suikerrietmateriaal Braskem Groen PE SEB853/72
| Dichtheid (23°C): | 0.923 g/cm3 |
|---|---|
| Melt mass-flow rate (MFR) (190°C/2,16 kg): | 2.7 g/10 min |
| Het vormen temperatuur: | 170 -190 °C |
Polyethyleen LDPE Plastic pellets Suikerriet materiaal Groen PE Braskem SPB681
| Dichtheid (23°C): | 0.922 g/cm3 |
|---|---|
| Melt mass-flow rate (MFR) (190°C/2,16 kg): | 30,8 g/10 min |
| Het vormen temperatuur: | 170 -190 °C |