Biobased suikerriet polyethyleen LLDPE granulaten Braskem Groen PE SLH218
| Dichtheid (23°C): | 0.916 g/cm3 |
|---|---|
| Melt mass-flow rate (MFR) (190°C/2,16 kg): | 2.3 g/10 min |
| Verwerkingsmethode: | Geblazen film extrusie. |
Polyethyleen LLDPE Granulaat Biobased Sugarcane Braskem Groen PE SLL318
| Dichtheid (23°C): | 0.918 g/cm3 |
|---|---|
| Melt mass-flow rate (MFR) (190°C/2,16 kg): | 2.7 g/10 min |
| Het vormen temperatuur: | 170 -180 °C |
Petrothene® NA149000 LyondellBasell LDPE
| Dichtheid: | 0.919 g/cm3 |
|---|---|
| Smelte doorstroming (MFR) (190°C/2,16 kg): | 4 g/10 min |
| Verwerkingsprocédés: | Extrusie, geblazen film |
Talsox® 8010 Formosa Kunststof Hdpe
| Dichtheid: | 00,956 g/cm3 |
|---|---|
| Smelte massa-stroom (MFR) (190°C/2,16 kg) 0,05 g/10 min: | 1 g/10 min |
| Vervaardiging: | Taiwan Formosa Plastics |
Petrothene® NA206000 LyondellBasell LDPE
| Dichtheid: | 0.918 g/cm3 |
|---|---|
| Smelte doorstroming (MFR) (190°C/2,16 kg): | 14 g/10 min |
| Verwerkingsprocédés: | Extrusie, geblazen film |
Polyethyleen LDPE Plastic pellets Suikerriet materiaal Groen PE Braskem SPB681
| Dichtheid (23°C): | 0.922 g/cm3 |
|---|---|
| Melt mass-flow rate (MFR) (190°C/2,16 kg): | 30,8 g/10 min |
| Het vormen temperatuur: | 170 -190 °C |
Braskem Groen PE STS7006 LDPE Pellets Biobased Polyethyleengranules 0,925 G/Cm3
| Dichtheid (23°C): | 0.925 g/cm3 |
|---|---|
| Melt mass-flow rate (MFR) (190°C/2,16 kg): | 0.6 g/10 min |
| Het vormen temperatuur: | 170 -190 °C |
Petrothene® Na204000 Lyondellbasell LDPE
| Dichtheid: | 0.918 g/cm3 |
|---|---|
| Smelte doorstroming (MFR) (190°C/2,16 kg): | 7 g/10 min |
| Verwerkingsprocédés: | Extrusie, geblazen film |
Petrothene® Na209009 Lyondellbasell Ldpe
| Dichtheid: | 0.925 g/cm3 |
|---|---|
| Smelte doorstroming (MFR) (190°C/2,16 kg): | 23 g/10 min |
| Verwerkingsprocédés: | Extrusie, geblazen film |
Groen PE Braskem SBF0323/12HC Biobased Polyethyleengranules LDPE suikerrietmateriaal
| Dichtheid (23°C): | 0.923 g/cm3 |
|---|---|
| Melt mass-flow rate (MFR) (190°C/2,16 kg): | 0.32 g/10 min |
| Het vormen temperatuur: | 170 -190 °C |